HT-1480 STANDARD YELLOW ALL PURPOSE

HT-1480 STANDARD YELLOW ALL PURPOSE

UNITED’S # HT 1480 ALLOY is designed for 20K – 22 K yellow gold casting& fabrication, which produces a Standard Yellow color. This alloy is not recommended for 18 karat usage.

MELTING We do recommend pre-alloying all alloy and fine gold with aggressive stirring & fluxing to assure a uniform mixture.

Step : 1 Pre- Alloying (Fine gold + alloy) Temperature 1070° – 1120° C

1958° – 2048° F

Step : 2 Casting Temperature for 20K-22K Alloyed Grain 1040° – 1060° C

1904° – 1940° F

FLASK TEMPERATURE For Vacuum casting 676° – 730° C

Use higher range for 20K-22K 1250° – 1350° F

For Centrifugal casting 565° – 730° C

Use higher range for 20K-22K 1050° – 1350° F

United # HT 1480 standard yellow alloy is formulated for 20K to 23 K Standard Yellow Gold Casting and sheet, plate & wire fabrication giving a Standard Yellow color. Alloy # HT 1480 can be used for casting also.

This Alloy is not recommended for 18 Karat.

MELTING The # HT 1480 Standard Yellow Alloy and fine gold should be melted together in a clean crucible. Put alloy in the bottom of the crucible and fine gold on top. Initial melting temperature should be 1100º – 1120º C for 20K – 23K. Drop temperature somewhat before pouring as listed below. Boric acid flux may be used to keep the metal clean during the melting process. The metal should be mixed well with a stirring rod before pouring to assure a good mix.

POURING TEMP 20K – 23K – 1100º – 1110º C (2012º F – 2030º F)

FOR INGOTS